Authors The Effect of Cooling Rate on the Solutionizing of IN718 Superalloy Produced via Selective Laser Melting (SLM) MethodH. H. Dastgerdi - Iran University of Industries and Mines (IUIM), Tehran, Iran
M. O. Shabani - Department of Mining and Metallurgical Engineering, Amirkabir University of Technology, Tehran, Iran
Y. Shajari - Institute of Materials and Energy, Meshkin Dasht, Karaj, Iran
Abstract:In the present study, IN718 super alloy was produced by selective laser melting (SLM) method and was imposed under solution heat treatment at temperature of 1040°C for 2 hours. Three different environments, such as water, air and furnaces were used to cool the samples after complete solution. The results of microstructural studies conducted by optical microscopy (OM) and field emission scanning electron microscopy (FESEM) showed that intermetallic precipitates were formed during the process, disappear after solution. In order to complete the FESEM results, X-Ray diffraction (XRD) test showed that in at all cooling rates, the only remaining phases of matrix are the austenite (γ) and carbides, which their locations are between the grains according to the microscopic images. This issue indicates the proper selection of solution parameters and proper execution of solution process. The micro hardness test showed that doing solution treatment to reduce the volume fraction or completely remove the secondary phase leads to decreased hardness. By increasing cooling rate, the hardness of samples was reduced, so that the hardness of sample chilled in 30 % water was reduced compared to the sample before the heat treatment.
Keywords:IN718 Superalloy, Selective Laser Melting (SLM), Solution Heat Treatment, Microstructure, Hardness
COI code: JR_JEFM-3-1_003
how to cite to this paper:If you want to refer to this article in your research, you can easily use the following in the resources and references section:
Dastgerdi, H. H.; M. O. Shabani & Y. Shajari, 2019, The Effect of Cooling Rate on the Solutionizing of IN718 Superalloy Produced via Selective Laser Melting (SLM) Method, Journal of Environmental Friendly Materials 3 (1), https://www.civilica.com/Paper-JR_JEFM-JR_JEFM-3-1_003.htmlInside the text, wherever referred to or an achievement of this article is mentioned, after mentioning the article, inside the parental, the following specifications are written.
First Time: (Dastgerdi, H. H.; M. O. Shabani & Y. Shajari, 2019)
Second and more: (Dastgerdi; Shabani & Shajari, 2019)
For a complete overview of how to citation please review the following CIVILICA Guide (Citation)
The University/Research Center Information:
Type: state university
Paper No.: 414
in University Ranking and Scientometrics the Iranian universities and research centers are evaluated based on scientific papers.
Research Info Management
Export Citation info of this paper to research management softwares
New Related Papers
- Optimal design of planar and space trusses
- Assessment of ASCE 41-06 pushover procedure inperformance of concrete vertical irregular buildings
- Vibration control of an inclined sagged cable using two different passive systems, a comparative study
- Analytical study of break-off tests onconcrete
- Effect of damping ratio on the response of a baseisolated buildings
The Above articles are recently indexed in the related subjects
Iran Scientific Advertisment Netword
Share this paper
WHAT IS COI?
COI is a national code dedicated to all Iranian Conference and Journal Papers. the COI of each paper can be verified online.