Authors Investigation of Cr2O3-Al2O3 refractory hot corrosion behavior in glass meltHussain Mahzoun - MSc student, Department of Materials Science Engineering, Bu-Ali Sina University, Hamedan, Iran.
Shahab Kazemi - Assistant Professor, Department of Materials Science Engineering, Bu-Ali Sina University, Hamedan,Iran.
Abstract:In this study, hot corrosion of chromite- corundum refractory was an investigation in the soda-lime glass melt. The purpose of this study was to investigate the refractory corrosion behavior in the glass industry and its lifetime, as well as the effect of refractory on glass produced in the contacting of this refractory. Initial refractory studies including density, chemical analysis and elemental analysis also determined the cold crush In order to better identify the sample. The hot corrosion test of refractories was immersed in glass melt at 1400-1500 oC for 6, 8 and 10 hours in direct contact with molten. After time test samples were cold down in environment condition. It was observed that with increasing test time, the refractory weight 0.21, then 0.48 and finally decreased to 0.91 g, the refractory size was reduced by 0.1, 0.4, and 0.8 mm. Also, the area affected by the melt increased time 5, 5.1, and 5.2 mm, respectively. The dissolved elements in the melt caused a significant change in the color of the final glass. The diffusion elements in refractories did not overcome corrosion. The refractory corrosion rate with was increased by increasing the time of direct placement in the melt, respectively, increasing time, 1.6, 2.8 and 4.2 centimeters per year increased significantly.
Keywords:corrosion, Refractory, Cr2O3-Al2O3, glass melt, Soda-Lime glass
COI code: EMGBC01_003
how to cite to this paper:If you want to refer to this article in your research, you can easily use the following in the resources and references section:
Mahzoun, Hussain & Shahab Kazemi, 2019, Investigation of Cr2O3-Al2O3 refractory hot corrosion behavior in glass melt, first international conference on the development of material engineering technology, mining and geology, تهران, انجمن مديريت و مهندسي توسعه فناوري, https://www.civilica.com/Paper-EMGBC01-EMGBC01_003.htmlInside the text, wherever referred to or an achievement of this article is mentioned, after mentioning the article, inside the parental, the following specifications are written.
First Time: (Mahzoun, Hussain & Shahab Kazemi, 2019)
Second and more: (Mahzoun & Kazemi, 2019)
For a complete overview of how to citation please review the following CIVILICA Guide (Citation)
Research Info Management
Export Citation info of this paper to research management softwares
New Related Papers
- Nano-Polyoxotungstate [Cu20Cl(OH)24(H2O)12(P8W48O184)]25- supported on magnetic nanoparticles for oxidation of thioether mustard (HD) analogs
- Synthesis of composite nanofibers with magnetic nanoparticles polyacrylic acid and polyvinyl alcohol by electrospinning with remarkable water resistance
- Investigations on TiON Sputter Coated Wool Fabric with regard to their Microstructure and Antibacterial Properties
- Evaluation the Effect of Graphene Oxide as Nanofiller on Corrosion Protection Properties of Epoxy Coatings
- Investigation of Ca on the microstructural evolution and porosity analysis of ZK60 alloy in as-cast and extruded conditions
The Above articles are recently indexed in the related subjects
Iran Scientific Advertisment Netword
Share this paper
WHAT IS COI?
COI is a national code dedicated to all Iranian Conference and Journal Papers. the COI of each paper can be verified online.