Durability aspects of recycled aggregate mortar mixtures
Publish place: 10th International Congress on Civil Engineering
Publish Year: 1394
نوع سند: مقاله کنفرانسی
زبان: English
View: 908
This Paper With 12 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICCE10_0007
تاریخ نمایه سازی: 19 تیر 1394
Abstract:
In this study the effects of recycled glass and recycled concrete fine aggregates on the compressive strength, water absorption, chloride-ion penetration, freeze-thaw and sulfate resistance as well as ASR expansion of mortar mixtures were investigated comparatively. For this purpose, 9 different mortar mixtures were prepared by replacing 25, 50, 75 and 100 wt% of crushed-limestone fine aggregate with recycled aggregates. Test results demonstrated that, compared to the control mixture, compressive strength of the mortar mixture decreased with increasing the recycled aggregate replacement level. The transport properties of recycled concrete aggregate-containing mixture were lower than those of the other two series. Frost resistance of mortar mixture improved by using both of the recycled aggregates. ASR expansion increased with increasing recycled glass aggregate replacement level. Mortar mixtures containing more than 50% recycled concrete aggregate showed higher sulfate resistance than the control mixture. This was attributed to the accumulation of ettringite in pores of the RC aggregate resulting in lower expansion.
Keywords:
Authors
Ali Mardani-Aghabaglou
Department of Civil Engineering, Ege University, Bornova-Izmir, Turkey
Ahsanollah Beglarigale
Department of Civil Engineering, Dokuz Eylul University, Buca-Izmir, Turkey
Halit YazICI
Department of Civil Engineering, Dokuz Eylul University, Buca-Izmir, Turkey
Kambiz Ramyar
Department of Civil Engineering, Ege University, Bornova-Izmir, Turkey
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :