Effect of heat treatment on mechanical properties of Al 7075 T6
Publish place: کنفرانس بین المللی پژوهش در علوم و مهندسی
Publish Year: 1395
نوع سند: مقاله کنفرانسی
زبان: English
View: 781
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICRSIE01_172
تاریخ نمایه سازی: 25 آذر 1395
Abstract:
Among the compounds Al, Series 2*** and 7*** due to achieve the desired mechanical properties of particular importance Are important. In the meantime, heat treatable alloy Al7075 including climbing alloysIs having a hard sediment. One of the most common heat treatment cycles performed on Al7075T6 heat treatment there is. In this study, samples of Al7075 alloy initially in a separate step Homogenization, and then dissolved at a temperature of 470-485°C for time min75 It fits again in the T6 temperature of 130℃ 160,190 and 220°C Vbmdt time 4h and quenched in water under conditions of heat treatment were tested. The final data review and analysis They conclude that the optimum temperature for solution temperature 485℃ 130min duration of temperature Is optimal because there is not enough time for uniform distribution of alloying elements result in step T6 in Brinell hardness of 143.35 maximum 220℃ temperature is achieved.
Keywords:
Authors
Behnam Dehganzadeh
Payam Noor University of Tabriz
Rahimeh Ahmadinejad
Payam Noor University of Tabriz
Mehdi Hosseinzadeh Khanamiri
Payam Noor University of Tabriz
Sanam Abedini
Payam Noor University of TabrizTabriz Sahand University
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :