Microstructural evolution of ultrafine-grained austenite fabricated by severe plastic deformation in Fe-Ni-C alloy
Publish place: 1st International and 6th Joint Conference of Iranian Society of Metallurgical Engineers and the scientific community of Casting
Publish Year: 1391
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,136
This Paper With 12 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_356
تاریخ نمایه سازی: 8 بهمن 1391
Abstract:
In this paper, microstructure and mechanical properties of austenite in Fe-24Ni-0.3C alloy subjected to accumulative roll bonding (ARB) process and subsequent annealing were studied. After 6 cycles of ARB process, elongated ultrafine-grained (UFG) austenite with mean grain size of 300 nm was obtained. Annealing treatment of 6-cycle ARB processed austenite at temperatures from 773 to 873 K resulted in formation of partly and fully recrystallized austenites with mean grain sizes between 750 nm to 2.5 μm.
Keywords:
Ultrafine-grains , Transformation induced plasticity (TRIP) , Accumulative roll bonding (ARB) , Microstructure
Authors
Hamidreza Jafarian
School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST),
Ehsan Borhani
Department of Nano technology, Nano-Materials Science and Engineering group, Semnan University,
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :