Study of particles rearrangement in supersolidus liquid phase sintering of Cu-28Zn
Publish Year: 1392
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,121
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES07_079
تاریخ نمایه سازی: 28 آذر 1392
Abstract:
The aim of this study is evolution of influence of effective forces in Supersolidus Liquid Phase Sintering of Cu-28Zn alloy which causes heterogeneity in different sections of microstructure. For this purpose prealloyed Cu-28Zn powder was sintered at various temperatures, 840-890 ˚C, under nitrogen atmosphere for 60 minutes. Metallography and fractography studies revealed that small increase in sintering temperature as a consequence of creating different amount of liquid phase results in considerable particle rearrangement, and varieties in obtained grain size, zinc accumulation in grain boundaries, pores’ shape and size. As well as the effect of produced liquid phase amount, which is a function of sintering temperature, would be clear by comparing fracture morphology of diverse parts of sections. Finally, according to attained physical and mechanical properties, which were in a good agreement with achieved microstructure, optimum sintering temperature equal of 860 ˚C was determined.
Keywords:
prealloyed brass powder , supersolidus liquid phase sintering , microstructure changes , particle rearrangement , zinc accumulation
Authors
Mahboubeh Gharooni Jafari
Department of Materials Engineering, Sahand University of Technology
Mazyar Azadbeh
Department of Materials Engineering, Sahand University of Technology
Nadia Mehrjou
Department of Materials Engineering, Sahand University of Technology
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :