An investigation of carbon nanotubes effect on drilled-induced delamination and fatigue-life of GFRP composites using acoustic emission
Publish place: 26th Annual Conference of Mechanical Engineering
Publish Year: 1397
نوع سند: مقاله کنفرانسی
زبان: English
View: 571
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ISME26_633
تاریخ نمایه سازی: 30 دی 1397
Abstract:
In this paper, the effect of adding carbon nanotubes on drilled-induced delamination and fatigue-life of glass/epoxy composites is investigated. For this purpose,specimens by three different percent of nanotubes were made and were drilled under the same conditions. The delamination around the hole which was because of drilling was calculated. Then specimens were applied under quasi-static tension loading. They had approximately close strength. Finally, tension-tension fatigue tests were done and specimens had distinctly different fatigt1e—life. During tests, acoustic emission technique was used to validate the mechanical results and for more investigation of failure procedure. Result showed that acoustic emission technique could monitor the specimens’ mechanical behavior and predict well the failure time in specimens. The result showed that adding carbon nanotubes can reduce the drilled-indttced delamination and increase the fatigue-life. There was an exponential relationship between nanotubes percent with delamination factor and a linear relationship between the nanotubes percent and the number of fatigue cycles.
Keywords:
Authors
naeim akbari shahkhosrvi
’Department of Mechanical Engineering, Arnirkabir University
mehdi ahmadi najaf abadi
Department of Mechanical Engineering, Arnirkabir University
hossein heydari
Department ۰fMecham eaI Engineering, Tafresh University