Tribological effect of thermocycling on dental nano-composite
Publish Year: 1392
نوع سند: مقاله کنفرانسی
زبان: English
View: 789
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
WMECH02_098
تاریخ نمایه سازی: 21 تیر 1393
Abstract:
The effect of thermocycling on the tribological properties of a commercial dental nano-composite has been studied by using the nano-scratch experiment. For this purpose some disk specimens from Filtek Z350 XT (3M ESPE, Germany) nano-composite, each of the diameter 10 mm and the thickness 4 mm were prepared. Half of the specimens were stored in distilled water at ambient conditions and the other half were thermocycled in distilled water for 1000 cycles between temperatures 5°C and 55°C. The nano-scratch experiment was applied on both non-thermocycled and thermocycled specimens by using Triboscope system (Hysitron Inc., USA) and Berkovich indenter. The nano-scratch experiments were performed by both constant and increasing loads for each sample. Atomic force microscopy (AFM) images were taken from the scratch site for analyzing the surface deformation of the samples. The scratch profile, residual scratch depth, scratch hardness and critical scratch load were obtained from the nano-scratch test and AFM images. The results indicate that the residual scratch depth and the criticalscratch load of the thermocycled samples have been decreased compared to the non-thermocycled ones. However, the scratch hardness of the thermocycled samples has been increased in comparison to the non-thermocycled specimens.
Authors
A Karimzadeh
PhD Student
M. R Ayatollahi
Professor, Fatigue and Fracture Laboratory, Center of Excellence in Experimental Solid Mechanics and Dynamics, School of Mechanical Engineering, Iran University of Science and Technology, Tehran, ۱۶۸۴۶-۱۳۱۱۴, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :