Environmental effects on mechanical properties of glass/epoxy and fiber metal laminates, Part II: Isothermal aging
Publish place: Mechanics of Advanced Composite Structures، Vol: 4، Issue: 3
Publish Year: 1396
نوع سند: مقاله ژورنالی
زبان: English
View: 422
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_MACS-4-3_003
تاریخ نمایه سازی: 14 تیر 1399
Abstract:
The aim of this study is to investigate effects of isothermal aging on mechanical properties of fiber metal laminates (FMLs) and glass/epoxy composites. For this purpose, both materials were fabricated using the wet lay-up manufacturing technique under vacuum pressure. Both the glass/epoxy composites and the FML specimens were then subjected to isothermal aging (130°C, dried air) for up to 5 weeks. After the isothermal aging, the specimens’ weight loss, caused by thermo-oxidative conditioning, was evaluated. Bending and Charpy impact tests were conducted on both the unaged and aged specimens to examine the isothermal conditioning’s effect on the mechanical properties of studied materials. Experimental results revealed that isothermal aging severely affected impact strength in the form of embrittlement and reduced ductility. However, no significant reduction was found in the flexural stiffness of isothermally aged FML and glass/epoxy specimens.
Keywords:
Fiber metal laminates (FMLs) , Glass/epoxy composites , Iso-thermal aging , Impact properties , Flexural properties
Authors
Moslem Najafi
Department of Mechanical Engineering, University of Guilan
Reza Ansari
guilan university
Abolfazl Darvizeh
Department of Mechanical Engineering, University of Guilan
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :