K Saeidi - Postgraduate student
MI Karbasi - ۱Postgraduate student
A Monshi - Professor, Department of Materials Engineering, Isfahan University of Technology

WC reinforced FeCoNb matrix composite powders were produced by mechanical alloying of WC and elemental powder mixtures of Fe, Co, and Nb. The effect of WC content and milling time on the alloy formation in the (Fe-Co-Nb) system was investigated. Phase analysis, and microstructure of the samples were evaluated using XRD and SEM, techniques. The XRD results indicated that Co dissolves into iron after 5 hours milling. After 10 hr milling the grain size of carbide phase was reduced to less than 30 nm. Scanning Electron micrograph of the as milled samples showed that; well dispersed WC in the matrix phase was obtained after 10 hr of milling and each particle represented a fully homogenous nano grain (FeCo-Nb)WC composite.

composite powder, Fe-Co alloy, mechanical alloying, tungsten carbide