Temperature Effect on Creep and Fracture Behaviors of Nano-SiO2-composite and AlSi12Cu3Ni2MgFe Aluminum Alloy
Publish Year: 1399
نوع سند: مقاله ژورنالی
زبان: English
View: 308
This Paper With 11 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-33-8_016
تاریخ نمایه سازی: 4 شهریور 1399
Abstract:
In the presented article, the temperature effect was studied on creep properties and fracture behaviors of AlSi12Cu3Ni2MgFe aluminum-silicon alloys, unreinforced and reinforced with SiO2 nano-particles. For such objective, standard specimens were fabricated by gravity casting and stir-casting methods, for aluminum alloys and nano-composites, respectively. Then, force-controlled creep testing was performed on standard specimens at 250, 275 and 300°C, under 100 MPa. Then, to find failure mechanisms, the fracture surface of test samples was also analyzed by the field emission scanning electron microscopy. Experimental results depicted the temperature changed creep behaviors of both materials, effectively. Moreover, a significant improvement in creep properties was observed by reinforcing the aluminum matrix with nano-particles, besides a heat treatment process. Such an increase in the creep lifetime was higher at 300°C. In addition, the fracture surface investigation of both materials implied the same brittle behavior, with quasi-cleavage marks. The failure location changed from inside the intermetallic phase into boundaries of the intermetallic phase in the nano-composite.
Keywords:
Creep property , Piston aluminum alloy , Aluminum Alloy Matrix Nano-composite Temperature Effect , Fracture behavior
Authors
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :