Thermal Analysis and Microstructural Evaluation of Inconel ۷۳۸LC Superalloy Gas Turbine Blade
عنوان مقاله: Thermal Analysis and Microstructural Evaluation of Inconel ۷۳۸LC Superalloy Gas Turbine Blade
شناسه ملی مقاله: JR_JEFM-4-2_004
منتشر شده در در سال 1399
شناسه ملی مقاله: JR_JEFM-4-2_004
منتشر شده در در سال 1399
مشخصات نویسندگان مقاله:
Rayatpour M - Niroo Research Institute (NRI), Tehran, Iran
Lalegani Z - Niroo Research Institute (NRI), Tehran, Iran
خلاصه مقاله:
Rayatpour M - Niroo Research Institute (NRI), Tehran, Iran
Lalegani Z - Niroo Research Institute (NRI), Tehran, Iran
The operational temperature of a gas turbine blade made of IN۷۳۸LC superalloy was investigated. The component under evaluation was a first stage blade of a ۲۵MW power plant gas turbine with the gas temperature of ۹۴۳ in the first stage nozzle at the base load. The evaluation was carried out after ۱۶۰۰۰ h of operation in the mode of base load. To analyze the temperature distribution of the component, three ۳D-models of the blade were prepared, meshed and analyzed using CFD software. The results indicate the higher temperatures in the upper section of the leading edge during steady state operation of the blade.To evaluate the reliability of this analysis, intermetallic coarsening behavior was examined as the most important microstructural changes of the alloy after long term service exposure. This metallographic analysis also approves increasing in temperature with height of the airfoil section.
کلمات کلیدی: gas turbine, IN۷۳۸LC Superalloy, Gamma Prime Coarsening