Kinetics of Austenite Recrystallization during the Annealing of Cold-rolled Fe-Mn-Al-C Steel
Publish place: The Iranian Journal of Materials Forming، Vol: 7، Issue: 1
Publish Year: 1399
نوع سند: مقاله ژورنالی
زبان: English
View: 213
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMF-7-1_008
تاریخ نمایه سازی: 18 فروردین 1400
Abstract:
In the current study, the recrystallization behavior of 75% cold-rolled Fe-22Mn-10Al-1.4C steel during annealing at 750, 770, 790, 810, and 830°C was studied. X-ray diffraction patterns and optical microscopy were used to characterize microstructures. The Vickers Micro-hardness test was used to characterize recrystallization kinetics during annealing. Johnson-Mehl-Avrami-Kolmogorov (JMAK) model was used to evaluate the experimental data. The as-homogenized microstructure illustrated only austenite with a high fraction of annealing twins, and austenite to martensite phase transformation was not observed after quenching at a high temperature and also until high thickness reduction. Avrami exponent was decreased from 0.76 to 0.42, with increasing the annealing temperature from 750 to 830°C. The activation energy value was determined to be ~175 kJ/mol, which was slightly higher than the diffusion activation energy of carbon in austenite.
Keywords:
Authors
M. A. Sohrabizadeh
Department of Materials Engineering, Bu-Ali Sina University, Hamedan, Iran
Y. Mazaheri
Department of Materials Engineering, Bu-Ali Sina University, Hamedan, Iran
M. Sheikhi
Department of Materials Engineering, Bu-Ali Sina University, Hamedan, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :