Experimental Investigation on Fatigue Evaluation of Orthopaedic Locking Compression Plate
عنوان مقاله: Experimental Investigation on Fatigue Evaluation of Orthopaedic Locking Compression Plate
شناسه ملی مقاله: JR_ADMTL-11-4_005
منتشر شده در در سال 1397
شناسه ملی مقاله: JR_ADMTL-11-4_005
منتشر شده در در سال 1397
مشخصات نویسندگان مقاله:
Saenoddin Mohajerzadeh - Department of Mechanical Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
Khalil Farhangdoost - Department of Mechanical Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
Pedram Zamani - Department of Mechanical Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
Kamal Kolasangiani - Department of Mechanical Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
خلاصه مقاله:
Saenoddin Mohajerzadeh - Department of Mechanical Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
Khalil Farhangdoost - Department of Mechanical Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
Pedram Zamani - Department of Mechanical Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
Kamal Kolasangiani - Department of Mechanical Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
Locking compression plate (LCP) is a common orthopedic instrument for internal fixation and healing of bone trauma. It is important to study on mechanical behavior and failure investigation of LCP because its failure leads to lots of cost and pain to the patient. In this paper, fatigue life of an eight-hole tibia LCP is evaluated under flexural loading. A four-point bending jig is manufactured and fatigue tests are performed for different compression loads. Fatigue life cycles are investigated for compression loads of ۵۰۰, ۶۰۰, ۷۰۰, ۸۰۰, ۹۰۰ and ۱۰۰۰ N and relation between compression load and life cycles is estimated. ۱۲۵ walking days is estimated for the patient during treatment period according to life cycle results. Post failure analysis results on fracture surface revealed that the crack initiated from the edge of compression hole and propagated from lower to the upper surface of LCP according to beach marks. Finally, Scanning electron microscopy (SEM) on the fracture surface revealed striations as a proof of fatigue crack growth. The striation spacing near the crack initiation site is found to be smaller than this spacing far from the initiation zone. The fatigue crack propagation life is estimated as ۱۶۰۰ cycles according to the number of striation spacings.
کلمات کلیدی: Failure Analysis, Fatigue Life, Four-Point Bending, Locking Compression Plate, Striation Spacing