Effect of Processing Parameters on Properties of Friction Stir Welded Joints of Aluminium Alloys AA۷۰۷۵- T۶۵۱ and AA۶۰۶۱-T۶
Publish place: International Journal of Advanced Design and Manufacturing Technology، Vol: 10، Issue: 2
Publish Year: 1396
نوع سند: مقاله ژورنالی
زبان: English
View: 164
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ADMTL-10-2_009
تاریخ نمایه سازی: 18 اردیبهشت 1400
Abstract:
In the present investigation the mechanical behaviour of AA۷۰۷۵T۶۵۱ and AA۶۰۶۱T۶ aluminium alloys plates joined by friction stir welding (FSW) were evaluated. The effects of weld process parameter like tool rotation speed ۶۵۰-۱۰۰۰ rpm and weld speed ۳۰-۴۰mm/min with square trapezoidal pin profile on mechanical properties were investigated. The welded joints were tested by means of by X-ray radiography, tensile, hardness and optical microscopy testing. The radiography revealed the presence of internal in FS welds and observed that increasing transverse speed increases the occurrence of weld defects. The hardness was found to be mixed effect with respect to tool rotations and transverse speed for similar FSW joints. But in dissimilar FSW joints, hardness decreases with increasing tool speed and weld speed and it was strongly affected by precipitate distribution. Difference in grain size and distribution was observed for different ranges of rotation and weld speed.
Keywords:
Authors
H. S. Patil
Mechanical Department, GIDC Degree Engineering College Abrama, Gujarat, India
Neelsai Sharma Kairav Patel
UG Students, Mechanical Department, GIDC Degree Engineering College, Abrama, Gujarat, India
Abhishek Patel Viral Patel
UG Students, Mechanical Department, GIDC Degree Engineering, Abrama, Gujarat, India
Chetan Patil
Mechanical Department, PSE, Saki-Palsana, Gujarat, India
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :