A Novel Type of Alkaline Activator for Geopolymer Concrete Based on Class C Fly Ash

Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 445

This Paper With 13 Page And PDF Format Ready To Download

  • Certificate
  • من نویسنده این مقاله هستم

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این Paper:

شناسه ملی سند علمی:

JR_ARCE-3-1_001

تاریخ نمایه سازی: 17 خرداد 1400

Abstract:

In recent years, geopolymers, as a new class of green cement binders, have been considered as an environmental-friendly alternative to Ordinary Portland Cement (OPC) which can potentially reduce negative environmental impacts of OPC including: carbon footprint, energy consumption and etc. In this experimental research, effects of different alkaline activator solutions on the compressive, Tensile and flexural strengths, water absorption and resistance to acidic condition of fly-based Geopolymer Concrete (GPC) were investigated. Furthermore, a novel type of alkaline activator for GPC was introduced. In this regard, GPC specimens based on Class C fly ash were manufactured and cured in ۹۰ ˚C. The obtained results showed that addition of NaOH to the mix after ۳ min of mixing KOH and Na۲SiO۳ with dry components (۱/۳ of the total mixing duration) resulted in the highest compressive, tensile and flexural strengths as well as, the lowest water absorption capacity and weight loss under acidic condition, amongst other cases.

Keywords:

Authors

Alireza Esparham

Department of Civil Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran.

Amir Bahador Moradikhou

Department of Civil Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran.

مراجع و منابع این Paper:

لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :
  • [۱]- Moradikhou, A. B., Esparham, A., and Avanaki, M. J., ...
  • [۲]- Phummiphan, I., Horpibulsuk, S., Rachan, R., Arulrajah, A., Shen, ...
  • [۳]- . Haddad, R. H and Alshbuol, O., ۲۰۱۶, Production ...
  • [۴]- Moradikhou, A. B., Hosseini, M. H., Mousavi Kashi, A., ...
  • [۵]- Behnood, A. and Golafshani, E. M., ۲۰۱۸, Predicting the ...
  • [۶]- Assi, L. N., Eddie Deaver, E. and Ziehl, P., ...
  • [۷]- Andrejkovičová, S., Sudagar, A., Rocha, J., Patinha, C., Hajjaji, ...
  • [۸]- Chen, C., Habert, G., Bouzidi, Y. and Jullien, A., ...
  • [۹]- Bashir, I., Kapoor, K. and Sood, H., ۲۰۱۷, An ...
  • [۱۰]- Ekinci, E., Türkmen, İ., Kantarci, F. and Karakoç, M. ...
  • [۱۱]- Görhan, G. and Kürklü, G., ۲۰۱۴, The influence of ...
  • [۱۲]-Amnadnua, K., Tangchirapat, W. and Jaturapitakkul, C., ۲۰۱۳, Strength, water ...
  • [۱۳]- Duxson, P., Provis, J. L., Lukey, G. C. and ...
  • [۱۴]- Bagheri, A. and Nazari, A., ۲۰۱۴, Compressive strength of ...
  • [۱۵]- Fernandez-Jimenez, A., García-Lodeiro, I. and Palomo, A., ۲۰۰۷, Durability ...
  • [۱۶]- Cheng, T. W. and Chiu, J. P., ۲۰۰۳, Fire-resistant ...
  • [۱۷]- Sarker, P. K., Kelly, S. and Yao, Z., ۲۰۱۴, ...
  • [۱۸]- Zhang, H. Y., Kodur, V., Qi, S. L., Cao, ...
  • [۱۹]- Palomo, A., Blanco-Varela, M. T., Granizo, M., Puertas, F., ...
  • [۲۰]- Bakharev, T., Sanjayan, J. G. and Cheng, Y. B., ...
  • [۲۱]- Zhang, M., H. Guo, El-Korchi, T., Zhang, G. and ...
  • [۲۲]- Wallah, S. E., ۲۰۱۰, Creep Behaviour of Fly Ash-Based ...
  • [۲۳]- Moradikhou, A. B., Esparham, A. and Jamshidi Avanaki, M., ...
  • [۲۴]- Solanki, P. and Dasha, B., ۲۰۱۶, Mechanical properties of ...
  • [۲۵]- Etemadi, M., Pouraghajan, M. and Gharavi, H., ۲۰۲۰, Investigating ...
  • [۲۶]- Esparham, A., Moradikhou, A. B., and Jamshidi Avanaki, M., ...
  • [۲۷]- Mahboubi, B., Guo, Z. and Wu, H., ۲۰۱۹, Evaluation ...
  • [۲۸]- Xu, H. and Van Deventer, J. S. J., ۲۰۰۰, ...
  • [۲۹]- A. Palomo, M.W. Grutzeck and M.T. Blanco, Alkali-activated fly ...
  • [۳۰]- Sharma, A. and Ahmad, J., ۲۰۱۷, Experimental study of ...
  • [۳۱]- Parveen, D. and Singhal, D., ۲۰۱۷, Development of mix ...
  • [۳۲]-Patel, Y. J. and Shah, N., ۲۰۱۸, Development of self-compacting ...
  • [۳۳]- Petrus, H. T. B. M., Hulu, J., Dalton, G. ...
  • [۳۴]- Sanni, S. H. and Khadiranaikar, R. B., ۲۰۱۳, Performance ...
  • [۳۵]- Raijiwala, D. B., Patil, H. S. and Kundan, I. ...
  • [۳۶]- Wang, H., Li, H. and Yan, F., ۲۰۰۵, Synthesis ...
  • [۳۷]- Mishra, A., Choudhary, D., Jain, N., Kumar, M., Sharda, ...
  • [۳۸]- Morsy, M., Alsayed, S., Al-Salloum, Y. and Almusallam, T., ...
  • [۳۹]-ASTM C۳۳ / C۳۳M-۱۸, ۲۰۱۸, Standard Specification for Concrete Aggregates, ...
  • [۴۰]-ASTM C۱۲۷-۱۵, ۲۰۱۵, Standard Test Method for Relative Density (Specific ...
  • [۴۱]-ASTM C۱۲۸-۱۵, ۲۰۱۵, Standard Test Method for Relative Density (Specific ...
  • [۴۲]-ASTM C۱۳۶ / C۱۳۶M-۱۴, ۲۰۱۴, Standard Test Method for Sieve ...
  • [۴۳]-ASTM D۲۴۱۹-۱۴, ۲۰۱۴, Standard Test Method for Sand Equivalent Value ...
  • [۴۴]-British Standards Institution, ۱۹۸۳, Testing Concrete: Method for Determination of ...
  • [۴۵]-ASTM C۴۹۶ / C۴۹۶M-۱۷, ۲۰۱۷, Standard Test Method for Splitting ...
  • [۴۶]-ASTM C۲۹۳ / C۲۹۳M-۱۶, ۲۰۱۶, Standard Test Method for Flexural ...
  • [۴۷]-ASTM C۶۴۲-۱۳, ۲۰۱۳, Standard Test Method for Density, Absorption, and ...
  • [۴۸]- Komnitsas, K., Zaharaki, D. and Perdikatsis, V., ۲۰۰۹, Effect ...
  • [۴۹]- Panagiotopoulou, C., Kakali, G., Tsivilis, S., Perraki, T. and ...
  • نمایش کامل مراجع