Fabrication of anodic aluminium oxide template and the generation of magnetic Co nanowires within it
Publish Year: 1398
نوع سند: مقاله ژورنالی
زبان: English
View: 231
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-7-4_006
تاریخ نمایه سازی: 9 مرداد 1400
Abstract:
Among nanostructured materials, magnetic nanowires have been heeded because of their high shape anisotropy and their easy fabrication methods. Electrochemical deposition on the anodic aluminium oxide (AAO) is one of the best methods to grow different nanowires. In this paper, the AAO was fabricated on the ۱۱۰۰ Al alloy substrate by hard anodizing in ۰.۳ M oxalic acid solution. Then, a barrier layer thinning process was carried out for the electrodeposition process. A pulsed electrodeposition process was used to fill the nano-pores. According to this method, cobalt nanowires were grown in the nano-holes. Structural, crystalline, and magnetic properties of the samples were evaluated using field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), and vibrating sample magnetometer (VSM), respectively. The results showed that nanowires have a diameter of ۸۷ nm and crystalline structure with crystalline plates in directions (۱۰۰), (۰۰۲), and (۱۱۰). A coercivity value of ۶۰۰ Oe was obtained for nanowires, which is several times larger than cobalt bulk.
Keywords:
Authors
masoud soltani
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Reihane Aliramezani
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
saeid akhavan
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Zeinab Erfani Gahrouei
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
mohammad noormohammadi
Department of Physics, Kashan University, Kashan, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :