Synthesis and Consolidation of Ag/ZnO Composite Powders via SPS Method
Publish place: The Iranian Journal of Materials Forming، Vol: 8، Issue: 3
Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 129
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMF-8-3_004
تاریخ نمایه سازی: 12 مرداد 1400
Abstract:
The present research was conducted to synthesize and densify Ag/۸wt.% ZnO composites via co-precipitation and spark plasma sintering (SPS) methods. The initial precipitates were precipitated by adding ammonium hydrogen carbonate solution to a solution mixture of silver and zinc nitrate. The precipitates were characterized by using the particle size analyzer and X-ray diffraction techniques. The precipitates were calcined at ۵۰۰°C and consolidated with SPS method for ۵ and ۱۰ min at ۵۴۰°C under ۳۵ MPa in vacuum. The results showed that rearrangement and bulk deformation had a significant effect on densification of the composite powders. The scanning electron microscopy investigations revealed that the SPSed composites had nearly dense microstructures with homogenous and fine dispersion of ZnO particles within the silver matrix. Moreover, it was confirmed that prolonging the sintering time from ۵ to ۱۰ min had no significant effect on the microstructure, relative density and hardness of the samples. Composites with relative densities above ۹۹% and ۶۲ HV hardness were synthesized through the applied procedure.
Keywords:
Authors
Mohammad Ardestani
Department of Materials Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :