masoud soltani - Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Ali Shafyei - Associate Professor of Materials Engineering, Isfahan University of Technology, Iran
Kianoush Zarrin naghsh - Department of material engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran.
Reihane Aliramezani - Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran

Copper is relatively soft metal and its wear and corrosion are considered to be a major factors of degradation of this metal. For this reason, when the higher wear and corrosion properties are needed, surface properties should be improved with different surface treatments. One of these methods is the applying of Ni-P electroless coating due to good mechanical properties, suitable corrosion resistance and its ability of heat treatment on Cu. In this research after the surface preparation of Cu, which included grinding, degreasing and surface activation, the specimens were dipped into commercial electroless nickel bath (SLOTONIP ۷۰A) for ۶۰ minutes. SEM images and the results of the EDS test confirmed the formation of Ni-P electroless coating (with ۱۰.۸۳ wt. % phosphorus) with a spherical structure. Applying the heat treatment increased the hardness from ۴۹۵ to ۸۸۰ Vickers. XRD results showed this hardening is due to the formation of Ni crystal and Ni۳P phases at this temperature in the coating. The study of wear resistance and corrosion property of coatings was also done using pin-on test and polarization tests, respectively. The results showed that the heat treatment improved the wear resistance of the coating, and the weight loss in the presence of the heat treated coating reduced to ۷۶% due to increasing hardness and roughness of the coating by performing heat treatment.

Ni-P electroless, Wear, Hardness, Heat treatment, polarization