Bimetal friction stir welding of aluminum to magnesium
Publish Year: 1392
نوع سند: مقاله ژورنالی
زبان: English
View: 92
This Paper With 12 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-1-1_004
تاریخ نمایه سازی: 12 مهر 1400
Abstract:
FSW material flow and phase transformation were studied at the interface of dissimilar welding of Al ۶۰۱۳ to Mg. Defect free butt weld was obtained when aluminum and magnesium test plates were placed in the advancing side and retreating side respectively, and the tool was placed ۱ mm off the weld centerline into the aluminum side. In order to understand how the materials flow during FSW, steel shots were implanted as indexes into the test plate’s intimate face and welding was performed with determined optimum parameters. X-ray images were used to evaluate secondary positions of the steel shots at weld zone. It was revealed that steel shots implanted in the advancing side test plate were penetrated from advancing side into the retreating side with a relatively large rotational displacement of α. But shots implanted in retreating side test plate remained only in retreating side, without penetrating into the advancing side, and displaced by a low angle of β. It could be concluded that to reach defect free welds by FSW between two dissimilar metals, the tool should be inserted in harder metal and harder metal should be placed in the advancing side too. EDS analysis was performed in order to study formation and distribution of intermetallic phases in the welds interface. Two intermetallic compounds formed sequentially at Al۶۰۱۳/Mg interface were Al۳Mg۲ and Al۱۲Mg۱۷ in weld condition. Welded specimens were heat treated and their effects on mechanical properties of welds and formation of new intermetallic layers were investigated.
Keywords:
Authors
P Pourahmad
Department of materials science and engineering, Karaj Branch, Islamic Azad University, Iran
M Abbasi
Department of materials science and engineering, Karaj Branch, Islamic Azad University, Iran
H.A Mehrabi
Department of materials science and engineering, Karaj Branch, Islamic Azad University, Iran