Sol-gel synthesis and characterization of alumina-۱۵%mullite composite nanopowder
Publish Year: 1393
نوع سند: مقاله ژورنالی
زبان: English
View: 170
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-2-1_004
تاریخ نمایه سازی: 12 مهر 1400
Abstract:
Homogeneous distribution of mullite in the matrix of alumina can be obtained through sol-gel method. In this work, nanopowder of alumina-mullite composite was synthesized with high homogeneity and high purity. So aluminum chloride hexahydrate and tetraethyl orthosilicate were used instead of alumina or mullite nanopowder. Studying the simultaneouse thermal analysis (STA) of mullite precursor reveals two endothermic peaks at ۱۴۵ and ۲۴۰°C due to dehydration and removal of the molecular water and the chloride component. An exothermic peak is also detected at ۸۵۵°C. According to the XRD patterns of alumina-۱۵vol.% mullite precursors calcined at different temperatures, crystallization of transitional alumina phases (γ, κ) occurs approximately at ۸۰۰°C. Then these phases transform to α alumina approximately at ۱۰۰۰°C. XRD patterns of alumina-۱۵%vol. mullite which were calcined at different temperatures show peaks of mullite relating to ۱۰۰۰°C. The specific surface area of this nanopowder calcined at ۹۰۰°C was calculated to be ۱۲۰.۹±۰.۵ m۲/g. The nanopowder was observed by TEM.
Keywords:
Authors
Ali Sedaghat
Department of Ceramic, Material and Energy Research Center, karaj, Iran.
E. Taheri-Nassaj
Department of Materials Engineering, Tarbiat Modares University, Tehran, Iran.
G. Soraru
Department of Materials Engineering and Industrial Technology, University of Trento, Trento, Italy.
R. Ceccatob
Department of Materials Engineering and Industrial Technology, University of Trento, Trento, Italy.
T. Ebadzadeh
Department of Ceramic, Material and Energy Research Center, karaj, Iran.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :