Fatigue and corrosion fatigue properties of Ti-۶Al-۴V implant grade titanium alloy in Ringer solution
Publish Year: 1396
نوع سند: مقاله ژورنالی
زبان: English
View: 127
This Paper With 11 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-5-3_002
تاریخ نمایه سازی: 12 مهر 1400
Abstract:
Nowadays modification of metallic biomaterials which are used as implants for bone and hard tissues replacement is considered as an important subject. In the current study, corrosion fatigue properties of Ti-۶Al-۴V alloy investigated via Rotating-Bending standard test method and then, the results compared with the fatigue properties of the specimens tested in the same conditions. Scanning electron microscopy used to investigate the chemical composition (EDS- Energy-dispersive X-ray spectroscopy), microstructural features and crack propagation characteristics. Results showed that the presence of corrosive environment not only results in decrease in fatigue life, but also eliminates the fatigue limit. Further studies revealed that aggregation of corrosion products, with more hardness values, at the crack tip cause an obvious deviation of crack propagation from its main direction. Therefore, a tortuous crack path through the bulk of the specimens was detected concurrent with penetration of solution into the crack. In addition, dimensions and morphology of fatigue crack surfaces were completely different from corrosion fatigue cracks as well.
Keywords:
Authors
Mahmoud Hajisafari
Department of Metallurgy and Materials Engineering, Yazd Branch, Islamic Azad University, Yazd, Iran
Arman Zare Bidaki
Department of Metallurgy and Materials Engineering, Yazd Branch, Islamic Azad University, Yazd, Iran
Saeid Yazdani
Department of Metallurgy and Materials Engineering, Yazd Branch, Islamic Azad University, Yazd, Iran