Manufactured single crystal components using Ni-base super alloys are routinely used in the hot sections of aero engines and industrial gas turbines due to their outstanding high temperature strength, toughness and resistance to degradation in corrosive and oxidative environments. To control the quality of the single crystal turbine blades, particular attention has been paid to grain selection, which is used to obtain the single crystal morphology from a plethora of columnar grains. For this purpose, different designs of grain selectors are employed and the most common type is the spiral grain selector. A typical spiral grain selector includes a starter block and a spiral (helix) located above. It has been found that the grains with orientation well aligned to the thermal gradient survive in the starter block by competitive grain growth while the selection of the single crystal grain occurs in the spiral part. In the present study, ۲Dspiral selectors with different geometries were designed and produced using a state-of-the-art Bridgeman Directional Solidification casting furnace to investigate the competitive growth during grain selection in ۲d grain selectors. The principal advantage of using a ۲-Dselector is to facilitate the wax injection process in investment casting by enabling significant degree of automation. The directional solidification process for obtaining single crystal component for Nickel Super alloys based on the competitive growth in ۲D and ۳D single crystal grain selector was experimentally investigated for various geometries. Transverse sections of the grain selectors using optical and EBSD microscopy techniques were observed to understand the competitive grain growth process.

Grain Selector, Single Crystal, Directional Solidification, CMSX-۴ Super alloys, Investment Casting