Role of Etching Process of SiC Particles on the Microstructure and Mechanical Properties of Stir Casted Al۳۵۷−SiC Metal matrix Composite
Publish place: Advanced Ceramics Progress، Vol: 7، Issue: 2
Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 201
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ACERPT-7-2_002
تاریخ نمایه سازی: 3 آبان 1400
Abstract:
Owing to their high strength-to-weight ratio, aluminum-ceramic composites, are widely used in various industries. In this study, aluminum matrix composite was fabricated with only ۲ wt% micron-sized SiC particles as the reinforcing phase using electromagnetic stir casting. Prior to mixing, the surface of SiC particles were chemically etched by HF, NaOH, and KOH at two heat treatment temperatures of ۴۶۰ and ۵۱۰ °C for ۳۰ min. The obtained results indicated better wettability and interaction between the etched SiC particles and Al matrix. In addition, etched SiC particle as a ceramic phase at ۴۶۰ °C enhanced the mechanical properties of Al as a metal matrix, such as enhancing hardness and E about of ۶.۶ and ۲۶.۶%, respectively, mainly due to the increasing inhibition against movement of dislocation confirmed by the observed brittle behavior of fracture surface.
Keywords:
Authors
A. Talezari
MS, Department of Materials Engineering, Faculty of Engineering, Malayer University, Malayer, Hamedan, Iran
A. R. Souri
Assistant Professor, Department of Materials Engineering, Faculty of Engineering, Malayer University, Malayer, Hamedan, Iran
A. Shanaghi
Associate Professor, Department of Materials Engineering, Faculty of Engineering, Malayer University, Malayer, Hamedan, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :