Polymeric Nanocomposite Membranes,Based on Sulfonated Poly(ether ether ketone) and Organically Modified Montmorillonite, as High-Performance Materials for Fuel Cell Applications
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,276
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
PPSRC2011_056
تاریخ نمایه سازی: 30 بهمن 1390
Abstract:
Poly(ether ether ketone) (PEEK) was sulfonated at various degrees with sulfuric acid .The optimum degree ofsulfonation was determined. In the next step various amount of different types of organically modifiedmontmorillonite (OMMTs), were introduced to the optimum sPEEK via the solution intercalation technique.The selectivity parameter – ratio of proton conductivity to methanol permeability– was identified and measured for each sample at 250c. the samples were determined by X-Ray diffraction to show the dispersion of differenet OMMTs in membranes. Finally the membrane based on sPEEK / MMT 1%(cloisite30B),as the optimum nano clay composition, exhibits a high selectivity andpower density at the concentrated methanol feed. Moreover, the optimum nanocompositemembrane compared to Nafion®117 membranes. It is found that the optimum nanocomposite membrane not only provides higher performance in comparisonto the neat sPEEK and Nafion®117 membranes, but also exhibits a high open circuit voltage (OCV) at theelevated methanol concentration.
Keywords:
Methanol fuel cell , Polyelectrolyte membrane , Sulfonated poly(ether ether ketone) , Polymer–clay nanocomposites , Montmorillonite
Authors
SeyyedEmadodin Shakeri
Department of Polymer Engineering and Color Technology, Amirkabir University of Technology, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :