Effect of zirconia addition on the properties of dolomite magnesia refractories used in steel industries
عنوان مقاله: Effect of zirconia addition on the properties of dolomite magnesia refractories used in steel industries
شناسه ملی مقاله: JR_ISSIRAN-18-1_004
منتشر شده در در سال 1400
شناسه ملی مقاله: JR_ISSIRAN-18-1_004
منتشر شده در در سال 1400
مشخصات نویسندگان مقاله:
فرناز آسا - Modern Ceramic Materials Institute, ACECR, Yazd, Iran
لیلا شریفی - Modern Ceramic Materials Institute, ACECR, Yazd, Iran
سیدحسین میرحسینی - Modern Ceramic Materials Institute, ACECR, Yazd, Iran
حسین عجمین - Modern Ceramic Materials Institute, ACECR, Yazd, Iran
آرش اعتماد - University of Yazd
خلاصه مقاله:
فرناز آسا - Modern Ceramic Materials Institute, ACECR, Yazd, Iran
لیلا شریفی - Modern Ceramic Materials Institute, ACECR, Yazd, Iran
سیدحسین میرحسینی - Modern Ceramic Materials Institute, ACECR, Yazd, Iran
حسین عجمین - Modern Ceramic Materials Institute, ACECR, Yazd, Iran
آرش اعتماد - University of Yazd
In this study, the influence of the zirconia addition on the properties and microstructure of alkali magnesia refractories without chrome band spinels was investigated. For this purpose, a primary formula based on magnesia and alumina to form spinel was considered, and different amounts of zirconia were added to achieve various samples. After thermal treatment at ۱۵۰۰ ̊C and ۱۶۰۰ ̊C, the physical and mechanical properties of fabricated samples such as density, apparent porosity, cold compressive and bending strength, refractoriness under load, and warm modulus of rupture according to ASTM were evaluated. The physical and mechanical properties of zirconia contained samples revealed that the addition of zirconia led to the formation of zirconate-based phases like magnesium zirconate, and calcium zirconate. This phase can be expanded by the thermal stresses due to its thermal mismatch with the phases of the field and improved the mechanical properties by creating microcracks in the structure. Addition of ۲% by weight of zirconia increased the density from ۲.۸ g/cm۳ to ۲.۹۵ g/cm۳ at ۱۶۰۰ °C. Compressive strength also increased from ۳۱۵ kg/cm۲ to ۵۵۰ kg/cm۲ and flexural strength from ۳۵ kg/cm۲ to ۶۵ kg/cm۲.
کلمات کلیدی: Refractories material, Magnesia alkaline brick, Zirconia, Spinel phase