Preparation of Cobalt Oxide/Zinc Oxide Nanocomposite
Publish Year: 1389
نوع سند: مقاله ژورنالی
زبان: English
View: 109
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-23-2_004
تاریخ نمایه سازی: 18 بهمن 1400
Abstract:
Cobalt Oxide/ Zinc Oxide nanocomposite was synthesized by dropwise addition ofCo(NO)۳.۶H۲O and Zn(NO۳)۲.۴H۲O solutions to KOH solution at different temperatures followed bycalcination at ۳۰۰ºC for ۴ h. The morphology and structure of nanoparticles and the influence oftemperature on particle size were studied using scanning electron microscopy (SEM) and X-RayDiffraction (XRD). Minimum particle size was obtained before calcination at ۷۰ºC. In addition, thespherical, semispherical and flake-shaped nanoparticles were observed at ambient temperature. Onthe other hand, Co(OH)۲ was transformed to Co۳O۴, ZnO flakes were eliminated, and particle sizechanged during calcination. Synthesized samples at ۵۰ºC and ۷۰ºC showed an increase size aftercalcinations; however, elimination of flakes during calcination caused particle size reduction forsynthesized sample at ambient temperature.
Authors
S. Alibeigi
materials department, KNTU
M.R. Vaezi
Nanotechnology and Advanced Materials Department, Material and Energy Research Center(MERC)
L. Nikzad
Research Center of Advanced Materials, Merc
A. Esmaielzadeh Kandjani
Applied Science, RMIT - RMIT University