A research on the corrosion inhibition of mild steel pitting corrosion in concrete pore solution by sodium nitrite was carried out by employing potentiodynamic, potentiostatic polarization and zero resistance ammetery (ZRA) techniques. Passivity breakdown potential was decreased from the transpassive potential of ۷۰۰ mV at the absence of chloride to a value of -۵۰ mV when just ۰.۰۱M NaCl was added to the test solution and further a decrease to -۳۵۰ mV was recorded when the concentration of chloride was increased to ۰.۵M. Addition of NaNO۲ into the saturated Ca(OH)۲ solution containing ۰.۵M NaCl considerably shifted the pitting potential towards noble values. Similar results of inhibitive effect of nitrite were obtained from couple potential and current measurement between two nominal identical electrodes through ZRA establishment. In the test solution containing NaNO۲, continuous increasing of the corrosion potential towards noble values and simultaneous decrease in couple current density towards zero proved the stability and improvement of the passive film. Whereas, continuous decrease in couple potential accompanied with sharp increase in couple current density with a stable value of ۳µA/cm۲ at the absence of NaNO۲ demonstrated the occurrence of pitting corrosion.

Concrete Pore Solution, Zero Resistance Ammetery (ZRA), Pitting Corrosion, Sodium Nitrite