Crack Behavior of the Aluminum Alloy ۲۰۲۴ Under Fretting Conditions
عنوان مقاله: Crack Behavior of the Aluminum Alloy ۲۰۲۴ Under Fretting Conditions
شناسه ملی مقاله: JR_IJE-15-3_007
منتشر شده در Volume ۱۵, Issue ۳, TRANSACTIONS A: Basics در سال 1381
شناسه ملی مقاله: JR_IJE-15-3_007
منتشر شده در Volume ۱۵, Issue ۳, TRANSACTIONS A: Basics در سال 1381
مشخصات نویسندگان مقاله:
G. H. Majzoobi - Engineering, Buali Sina University
G. H. Farrahi - School of Mechanical Engineering, Sharif University of Technology
خلاصه مقاله:
G. H. Majzoobi - Engineering, Buali Sina University
G. H. Farrahi - School of Mechanical Engineering, Sharif University of Technology
The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy ۲۰۲۴ was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact surface and the stress intensity factor. The results showed that tensile stress maxima are situated at the trailing edge of the contact zone. Experimental results showed that the crack initiates from the trailing edge of the contact zone too. The crack extension angle was calculated and compared with experimental results at different normal loads. The stress intensity factor increased with increasing friction. The crack initially grows in combined mode I and II before deflecting to mode I plane. Delamination, one of the wear mechanisms, has been observed in our experiments too.
کلمات کلیدی: Fretting Fatigue, Crack Growth, Delamination, Aluminum, Finite elements
صفحه اختصاصی مقاله و دریافت فایل کامل: https://civilica.com/doc/1415762/