Ghanbar Ebrahimi - Natural Resources, Sharif University of Technology
Robert H. Falk - Forest Products Laboratory,, USDA Forest Service
Mehdi Tajvidi - Natural Resources, University of Tehran
M. Behzad - Mechanical Engineering, Sharif University of Technology

In this study, effect of MAPE (maleic anhydride polyethylene) as the compatibilizer on the mechanical properties of wood-flour polyethylene composites has been investigated by using Dynamic Mechanical Analysis (DMA). Composites were made at ۲۵% and ۵۰% by weight fiber contents and ۱% and ۲% compatibilizer respectively. Controls were also made at the same fiber contents without the compatibilizer. Static mechanical tests including tensile and bending tests were performed. Temperature scans in the range of -۱۱۰ to +۱۰۰°C was also conducted. Results indicated improvements in the mechanical properties due to the compatibilizer addition. Storage modulus values were higher in the case of coupled composites especially at ۵۰% fiber loading. Glass transition was hard to detect in all composite systems while increasing fiber content slightly shifted alpha transition to higher temperatures. MAPE had negligible effects on the main transitions but the effect of fiber content on the intensity and temperature of alpha transition seemed to be proportional to the fiber content. Mechanical loss factor spectra showed that at ۵۰% fiber content, the compatibilizer caused a reduction in tanδ values indicating less energy loss when the compatibilizer was present.

Composites, Wood flour, high, density Polypropylene, Compatibilizer, Dynamic Mechanical Analysis