Synthesis of TiC-Al۲O۳ Nanocomposite from Impure TiO۲ by Mechanical Activated Sintering
Publish Year: 1387
نوع سند: مقاله ژورنالی
زبان: English
View: 136
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-21-3_007
تاریخ نمایه سازی: 20 اسفند 1400
Abstract:
In this research, the production possibility of TiC-Al۲O۳ nanocomposite, as a useful ceramic from commercially pure TiO۲, aluminum powder and carbon black has been investigated. Routile (TiO۲) with carbon black and aluminum were placed in a high energy ball mill and sampled during different milling times. Then, the activated powders were synthesized at different temperatures in an atmosphere control tube furnace. Our results show that using this method has decreased the synthesizing temperature to ۱۰۰۰-۱۲۵۰˚C by increasing the milling time. Also the width of X-ray patterns peaks, had made it apparent that, the size of produced TiC crystals was in order of nanometer. Furthermore it was detected that the lattice parameter deviated slightly from the standard size.
Keywords:
Authors
Maziar Yaghmaee
Physics, MERC and SBU
Mansour Razavi
Materials Engineering, MERC
M. R. Rahimipour
Materials Engineering, Merc