Dissimilar electron beam welding of high temperature titanium alloys

Publish Year: 1400
نوع سند: مقاله کنفرانسی
زبان: English
View: 129

This Paper With 10 Page And PDF Format Ready To Download

  • Certificate
  • من نویسنده این مقاله هستم

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این Paper:

شناسه ملی سند علمی:

INCWI22_043

تاریخ نمایه سازی: 16 فروردین 1401

Abstract:

Electron beam welding was applied to join dissimilar Ti۵۵/TA۱۵ high temperature titanium alloys. Defect-free joints were obtained. Microstructure observation via optical and electron microscopes showed that FZ consisted of martensite α΄ and acicular α. The HAZ of both Ti۵۵ and TA۱۵ sides consisted of two regions; LT-HAZ consisted of primary α, secondary α and prior β and HT-HAZ mainly composed of martensite α΄ and acicular α. In addition, a characteristic asymmetrical microhardness profile was observed in dissimilar welded joints lower hardness of fusion zone rather than HAZ of both Ti۵۵ and TA۱۵ alloys.Room temperature tensile test results represented slightly weakness of weld metal compared to the Ti۵۵ and TA۱۵ alloys, however, good strength of welded joint at high temperature test results was achieved.

Authors

Vahid Esfahani Yeganeh

Institute of Materials and Energy, Iranian Space Research Centre, Isfahan, Iran