Removal of Cefixime Using Heterogeneous Fenton Catalysts: Alginate/Magnetite Hydroxyapatite Nanocomposite
Publish Year: 1401
نوع سند: مقاله ژورنالی
زبان: English
View: 159
This Paper With 17 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JWENT-7-1_002
تاریخ نمایه سازی: 28 فروردین 1401
Abstract:
In this study, alginate, magnetite, and hydroxyapatite were used to fabricate alginate-hydroxyapatite (Alg-Hap), alginate-Fe۳O۴ (Alg-Fe۳O۴), and alginate-magnetic hydroxyapatite (Alg-mHap) using ferric chloride (III) crosslinker to remove cefixime from an aqueous solution. FTIR, SEM, VSM, BET, and XRD tests were used to determine the functional groups, morphology, magnetization behavior, surface area, and crystallinity of catalysts, respectively. The optimal pH for the Fenton reaction was determined to be ۳.۳ for Alg-Hap and Alg-Fe۳O۴ catalysts and ۴ for Alg-mHap catalysts. Increases in the concentration of hydrogen peroxide (۱ to ۳ mM) and the amount of catalyst (۵۰ to ۹۰ gr/L) increased the percentage of degradation to approximately ۸% and ۶%, respectively. The degradation efficiency of cefixime by using Alg-mHap as the best catalyst in the Fenton process was achieved ۹۱%, at optimum condition (pH of ۴, catalyst amount of ۹۰ gr/L, initial cefixime concentration of ۵ mg/L, H۲O۲ concentration of ۳ mM within ۹۰ min). Moreover, the second-order kinetic equation fits the experimental data for cefixime degradation for all three catalysts. Furthermore, not only did the catalysts display a negligible iron leaching (۰.۹۲ mg/L for Alg-mHap) but also after three consecutive cycles, the catalysts indicated long-term stability. Comparison between synthesized catalysts and other methods proved its effectiveness.
Keywords:
Authors
Mona Nabizad
Chemical Engineering Department, Engineering Faculty, University of Guilan, Rasht, Iran
Ahmad Dadvand Koohi
Chemical Engineering Department, University of Guilan. Rasht, Iran
Zahra Erfanipour
Chemical Engineering Department, Engineering Faculty, University of Guilan, Rasht, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :