Synthesis, characterization and comparative study of aromatic polyureas based on ۲, ۳-dihydro-۱, ۴-phthalazinedione with various aromatic and aliphatic diisocyanates
عنوان مقاله: Synthesis, characterization and comparative study of aromatic polyureas based on ۲, ۳-dihydro-۱, ۴-phthalazinedione with various aromatic and aliphatic diisocyanates
شناسه ملی مقاله: JR_AJGC-6-2_004
منتشر شده در در سال 1401
شناسه ملی مقاله: JR_AJGC-6-2_004
منتشر شده در در سال 1401
مشخصات نویسندگان مقاله:
Sanaz Mohammadzadeh Koumleh - Department of Chemistry, Shahrood University of Technology, Shahrood, Iran
Shahrzad Rahmani - Department of Chemical Engineering, Babol Noshirvani University of Technology, Babol, Iran
Hosein Nasr-Isfahani - Department of Chemical Engineering, Babol Noshirvani University of Technology, Babol, Iran
خلاصه مقاله:
Sanaz Mohammadzadeh Koumleh - Department of Chemistry, Shahrood University of Technology, Shahrood, Iran
Shahrzad Rahmani - Department of Chemical Engineering, Babol Noshirvani University of Technology, Babol, Iran
Hosein Nasr-Isfahani - Department of Chemical Engineering, Babol Noshirvani University of Technology, Babol, Iran
Rigid aromatic backbone in high-performance polymers such as Kevlar has been known to be effective in their remarkable properties. Four new polyureas were synthesized based on the ۲, ۳-Dihydro-۱, ۴-phthalazinedione with various aromatic and aliphatic diisocyanates to mimic the properties of high-performance polymers with accessible monomers, facile synthesis procedures, and more economic. The chemical structure of polyureas was validated using Infrared spectroscopy (IR) and elemental analysis. Molecular weight was determined using the Mark-Houwink equation. Weight losses of these polyureas with temperature were determined by thermal gravimetric analysis (TGA). Depending on the structure of polyureas, that had an average melting temperature of ۱۵۳-۲۹۰ °C, Solubility parameters were calculated using the group molar attraction constants of Hoy. Polymers were almost insoluble in different solvents, as demonstrated by attempts to solubilize in several solvents at ۴۰ °C.
کلمات کلیدی: Polyurea Phthalazinedione Aromatic Backbone Mark, Houwink Equation Group Molar Attraction Constants