Synthesis of hydroxyapatite nanoparticles trough polyelectrolyte-modified microemulsions
Publish place: International Journal of Nano Dimension، Vol: 3، Issue: 2
Publish Year: 1391
نوع سند: مقاله ژورنالی
زبان: English
View: 109
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJND-3-2_005
تاریخ نمایه سازی: 24 تیر 1401
Abstract:
The paper is focused on the formation of hydroxyapatite nanoparticles (HAp) in polyelectrolyte-modified microemulsions, in a microemulsion template phase consisting of cyclohexane, water, cationic surfactant and cosurfactant, in the presence of Na-polyacrylate (PAA) as an anionic polyelectrolyte. It is shown that PAA, can be incorporated into the individual inverse microemulsion droplets. The microemulsion droplets and PAA-filled microemulsion droplets can be successfully used as a template phase for the nanoparticles formation. Prepared HAp in presence of polyelectrolyte has a different morphology from samples which are synthesized in absence of polyelectrolyte. PAA leads to formation of needle-like HAp (۲۰-۳۰nm in diameter and ۱۰۰-۲۰۰nm in length). Formation of HAp at room temperature was confirmed by X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR). Size and morphology of the HAp samples were characterized using transmission electron microscopy (TEM).
Authors
K. Akhavan
Department of Chemistry, Faculty of science, Islamic Azad University, Rasht Branch, Rasht, Iran.