Preparation of surface modified magnetic Iron Oxide nanoparticles and study of their colloidal behavior

Publish Year: 1393
نوع سند: مقاله ژورنالی
زبان: English
View: 112

This Paper With 6 Page And PDF Format Ready To Download

  • Certificate
  • من نویسنده این مقاله هستم

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این Paper:

شناسه ملی سند علمی:

JR_IJND-5-3_010

تاریخ نمایه سازی: 24 تیر 1401

Abstract:

In this work, we report synthesis of surface modified superparamagnetic iron oxide nanoparticles (SPION) by co-precipitation method using FeSO۴.۷H۲O and Fe۲(SO۴)۳.۵H۲O as precursors and trisodium citrate dihydrate as surfactant. Surface modification of the as prepared samples was performed in pot by sol-gel precipitation method using tetraethoxysilane (TEOS). The structure, morphology, and magnetic properties of the products were characterized by X-ray powder diffraction (XRD), Scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FT-IR), and Vibrating sample magnetometer (VSM) at room temperature. The results revealed formation of iron oxide nanoparticles, with an average size parameter of ۸.۵ nm for naked and ۳۷nm for silica coated particles, with a superparamagnetic behavior and fast response to applied magnetic fields with zero remanence and coercivity.

Authors

M. Seyed Sadjadi

Department of Chemistry, Science and Research Branch, Islamic Azad University, Tehran ۱۴۷۷۸ ۹۲۸۵۵, Iran.

S. E. Babaei

Department of Chemistry, Science and Research Branch, Islamic Azad University, Tehran ۱۴۷۷۸ ۹۲۸۵۵, Iran.

N. Farhadyar

Department of Chemistry, Varamin –Pishva Branch, Islamic Azad University, Varamin, Iran.