Yarn pulling out test and numerical solution of penetration into woven fabric target impregnated with shear thickening fluid using SiO۲ /Polyethylene Glycol
Publish place: International Journal of Nano Dimension، Vol: 6، Issue: 4
Publish Year: 1394
نوع سند: مقاله ژورنالی
زبان: English
View: 157
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJND-6-4_009
تاریخ نمایه سازی: 24 تیر 1401
Abstract:
In this paper, finite element model of woven fabric target has been investigated which is impacted by a cylindrical projectile. Fabrics are impregnated with Shear Thickening Fluid (STF). The effects of the (STF) have been considered as frictional effect. The STF has been made (Nano Silica and Polyethylene Glycol (PEG)) and then diluted by ethanol proportion of ۳:۱. Yarn pulling out test from inside of fabric is performed to estimate the pulling out force and the friction coefficient. The speed of pulling out was ۵۰۰ mm/min and the samples were placed vertically in tensile device. The results of yarn pulled out indicated that the fabric impregnated in STF needs more force in order to gets out of fabric. Friction coefficient of a regular fabric is ۰.۲۶ and in a fabric impregnated by STF is ۱.۵. Friction coefficients of tow fabric types of raw fabric and fabric with STF are entered in ANSYS software along with mechanical characteristic of a yarn. Ballistic range velocity was extracted for samples in software and was compared with experience results.
Keywords:
Shear Thickening Fluid (STF) , Yarn pulled up , Nano silica , Polyethylene glycol (PEG) , Friction coefficients
Authors
N. Kordani
Department of Mechanical Engineering, Mazandaran University, Mazandaran, Iran.
A. Sadough Vanini
Department of Mechanical Engineering, Amirkabir University of Technology, Tehran, Iran.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :