Surface, structural and optical investigation on Poly Vinyl Alcohol (PVA)/Bi۲WO۶ nanocomposite films
Publish place: International Journal of Nano Dimension، Vol: 13، Issue: 3
Publish Year: 1401
نوع سند: مقاله ژورنالی
زبان: English
View: 109
This Paper With 15 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJND-13-3_002
تاریخ نمایه سازی: 1 مرداد 1401
Abstract:
Bismuth tungstate (Bi۲WO۶) emerged as one of the most capable chromogenic compounds among transition metal oxide having wide opto-electronic applications. It is an n-type semiconducting material having bandgap around ~۲.۷eV. Conversely, NanoComposite (NC) materials have been investigated in order to tailor the properties polymers and also to widen the applications. In this context Poly (vinyl alcohol)/ Bismuth tungstate (PVA/Bi۲WO۳) NC films were prepared with various weight ratio of Bi۲WO۶ content viz.۰, ۰.۱, ۰.۲ ۰.۴, and ۰.۸ wt%. The solution combustion method was employed to prepare Bi۲WO۶ nanoparticles (NPs). Subsequently, synergistic effect of polymer matrix and Bi۲WO۶ NPs is characterized and analysed to estimate the enhanced properties. The surface morphology of the NC’s films was explored by Scanning Electron Microscopy (SEM). Elemental analysis is carried out using EDAX. The formation of polymer NC and its microstructural properties were investigated by X-ray diffraction technique and it is revealed that there is formation of orthorhombic phase for Bi۲WO۶ NPs with an average size of ۳۵nm. Interaction of NP and PVA is studied using FT-IR spectrometer. The optical constants were evaluated by UV-visible spectrometer and it was found that NC films bandgap energy varied from ۵.۴ eV to ۲.۸۵eV for direct and from ۴.۵۷eV to ۲.۳۸eV for indirect bandgap. It is anticipated that these unique organic–inorganic NC materials are the emerging functional materials in the field of opto-electronics.
Keywords:
Authors
Rashmi Saragur Nanjundaiah
Department of Industrial Production and Engineering, The National Institute of Engineering, Mysore- ۵۷۰ ۰۰۸, Karnataka, India.
Chandrashekar Hosur Kumara
Department of Industrial Production and Engineering, The National Institute of Engineering, Mysore- ۵۷۰ ۰۰۸, Karnataka, India.
Sangamesha Madanahalli Ankanathappa
Department of Chemistry, The National Institute of Engineering, Mysore- ۵۷۰ ۰۰۸, Karnataka, India.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :