Mehdi Shahedi Asl - Department of Mechanical Engineering, University of Mohaghegh Ardabili, Ardabil, Iran
Hekmat Razavizadeh - School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran

In this paper, the leaching of a sulfide concentrate, from “Sarcheshmeh Copper Complex”, by sulfuric acid is studied. The influences of sulfuric acid concentration and leaching temperature were scrutinized to optimize the processing parameters and to disclose the kinetics of the extraction process. The leaching rate of copper was not significantly improved with enhancing the temperature and concentration of sulfuric acid. The formation of elemental sulfur was found as a reducer of the leaching rate. Only ~۷۰% of copper was extracted by adding ۱M ferric sulfate as the oxidant agent, as well as increasing the leaching temperature up to ۸۵ °C. By leaching the mechanically activated concentrate in Fe۲(SO۴)۳-doped H۲SO۴ at ۸۵ °C, the amount of extracted copper was ~۹۰% after ۱۸۰ min. The experimental results were excellently fitted with the diffusion-controlled kinetic model as the activation energy of ~۲۷ kJ/mol was estimated.

Leaching, Copper, Sulfide concentrate, Ferric sulfate, Mechanical activation