The effect of adding nano-silica on the ultrasonic pulse velocity of geopolymer concrete

Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 69

This Paper With 7 Page And PDF Format Ready To Download

  • Certificate
  • من نویسنده این مقاله هستم

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این Paper:

شناسه ملی سند علمی:

JR_JPST-7-2_004

تاریخ نمایه سازی: 5 شهریور 1401

Abstract:

Nanotechnology plays an important role in the current construction industry. It has been observed that several properties of cement-based concrete are affected by different nano materials. In this study, different weight percentages of nano-silica (۰, ۱, ۲, and ۴ wt%) were used to build geopolymer specimens. The mechanical properties of the specimens were then measured, including the compressive and flexural strength. Results demonstrated that increasing the percentage of nano-silica from ۰ to ۴ wt% increases the compressive strength of the specimens from ۵۰.۴ to ۷۵.۲ MPa and the flexural strength from ۱۱.۴ to ۲۶.۲ MPa. Furthermore, it was observed that the ultrasonic pulse velocity was altered by increasing SiO۲ (nano-silica), decreasing the ultrasonic pulse rate from ۷.۰ to ۴.۵ km.s-۱.

Keywords:

Geopolymer concrete , Nano– silica , compressive and flexural strength , ultrasonic pulse velocity

Authors

Behzad Mehdikhani

Standard Research Institute, Technical and Engineering Faculty, Construction and Mineral Department, Karaj, Iran

Behzad Saeedi Razavi

Standard Research Institute, Technical and Engineering Faculty, Construction and Mineral Department, Karaj, Iran

Jamal Ahmadi

Department of Civil, Faculty of Engineering, University of Zanjan, Zanjan, Iran

Ali Goharrokhi

Applied Science Center of Khorasan Razavi Municipalities, Mashhad, Iran

مراجع و منابع این Paper:

لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :
  • S. Naskar, A.K. Chakrabort, Effect of nano materials in geopolymer ...
  • J. Davidovits, Properties of geopolymer cements, In Proceedings of the ...
  • A. Taffe, C. Maierhofer, Guidelines for NDT methods in Civil ...
  • A.M. Neville, J.J. Brooks, Concrete Technology, ۲nd Ed., Prentice Hall, ...
  • Y. Lin, H. Changfan, C. Hsiao, Estimation of high performance ...
  • Y. Lin, C.-P. Lai, T. Yen, Prediction of ultrasonic pulse ...
  • E.A. Whitehurst, Evaluation of concrete properties from sonic tests, American ...
  • T.R. Naik, V.M. Malhotra, J.S. Popovics, The ultrasonic pulse velocity ...
  • B.S. Al-Nu’man, B.R. Aziz, S.A. Abdulla, S.E. Khaleel, Compressive strength ...
  • P. Duxson, A. Fernández-Jiménez, J.L. Provis, G.C. Lukey, A. Palomo, ...
  • Z. Zidi, M. Ltifi, Z. Ben Ayadi, L. El Mir, ...
  • H.M.M. Khater, Physicomechanical properties of nano-silica effect on geopolymer composites, ...
  • Y. Tanigawa, K. Baba, H. Mori, Estimation of concrete strength ...
  • U. Durak, O. Karahan, B. Uzal, S. İlkentapar, C.D. Atiş, ...
  • J. Davidovits, Global warming impact on the cement and aggregates ...
  • H.M. Khater, Effect of nano-silica on microstructure formation of low-cost ...
  • O.A. Naniz, M. Mazloom, Effects of colloidal nano-silica on fresh ...
  • D. Adak, M. Sarkar, S. Mandal, Effect of nano-silica on ...
  • D. Tarangini, P. Sravana, P. Srinivasa Rao, Effect of nano ...
  • J. Davidovits, Geopolymer Chemistry and Applications, ۴th Ed., Geopolymer Institute, ...
  • M. Karimaei, F. Dabbaghi, M. Dehestani, M. Rashidi, Estimating compressive ...
  • نمایش کامل مراجع