Structural studies of nanosized nickel-substituted cobalt ferrite, synthesized by sol-gel method
Publish place: 3rd International Conference on Materials Heat Treatment
Publish Year: 1391
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,900
متن کامل این Paper منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل Paper (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICMH03_066
تاریخ نمایه سازی: 21 تیر 1391
Abstract:
In this study Ni substituted cobalt ferrite nanopowders Co1-xNixFe2O4 (x=0.1, 0.3, 0.5, 0.7 and 0.9) were prepared by sol-gel method. Phase identification of the samples was performed by X-ray diffraction (XRD) and mean crystallite sizes of 30 nm were calculated by Scherrerʾs formula. The results show that a minimum calcining temperature of 500 ºC is required to obtain a single phase spinel structure for all samples. It was observed that the lattice parameter of the samples decreases from 8.35 Å to 8.29 Å as Ni decreases. Magnetic measurements were carried out on cold pressed samples and the results show that as the value of x increases saturation magnetization decreases. Curie temperatures of the samples were measured and the results show that by increasing the x values the Curie temperatures of the samples increase. This increase was explained based on the change of superexchange interactions between different magnetic ions. Also the coercive forces of the samples were decreased by increasing x values which was explained based on the changes of anisotropy energy
Keywords:
Authors
Elnaz Darsheshdar
Physics Department, University of Isfahan, Isfahan, Iran
Morteza Mozaffari
Physics Department, Faculty of Science, Razi University, Kermanshah, Iran
Jamshid Amighian
Physics Department, Faculty of Science, University of Isfahan, Isfahan, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :