Effect of Yttrium Addition on Mechanical and Physical Properties of Ti۱۵Mo Alloy as an Implant Materia

عنوان مقاله: Effect of Yttrium Addition on Mechanical and Physical Properties of Ti۱۵Mo Alloy as an Implant Materia
شناسه ملی مقاله: JR_JMCH-6-5_006
منتشر شده در در سال 1402
مشخصات نویسندگان مقاله:

Yas Mohammed Musadaq - Department of Prosthodontics, College of Dentistry, University of Baghdad, Bab-Almoadham, P.O. Box ۱۴۱۷, Baghdad, Iraq
Ghassan Abdul-Hamid Naji - College of Dentistry, University of Baghdad, Baghdad, Iraq
Haydar H. J. Jamal Al‑Deen - Department of Metallurgical Engineering, Materials Engineering Faculty, University of Babylon, Hillah, Iraq

خلاصه مقاله:
The unique biomaterial multi-component Ti-Mo-xY (x = ۰.۵, ۱.۰, ۱.۵ wt. percent) alloys were created as a way to improve the mechanical characteristics and lessen the biomaterials’ toxicity for implants to create new biomaterials for implant applications. This study aims to look at how adding yttrium (Y) changes the alloy's microstructure and mechanical characteristics. Through the use of powder metallurgy, Ti-Mo-xY (x = ۰.۵, ۱.۰, and ۱.۵ wt. percent) alloys are created. Atmospheric pressure high-purity argon gas is used to sinter the metals. The Brinell hardness tester was used for the hardness test, and optical, scanning, and scanning electron microscopes were used to characterize the microstructure. Ti-Mo-xY (x = ۰.۵, ۱.۰, ۱.۵ wt. percent) alloys tested hardness at ۴۰۵.۳۳, ۴۳۵.۷۶, and ۵۱۰.۰۵ HB, respectively. Ti-Mo-xY alloys with the enhanced compressive strength had values of ۱۷.۸۲, ۱۸.۰۴, and ۱۸.۱۴ MPa (where x = ۰.۵, ۱.۰, or ۱.۵ weight percent). The yttrium addition can significantly improve the mechanical properties of powder-metallurgical Ti alloys. Its cause may be related to the removed oxygen from the matrix and the strengthening action of Y oxides.

کلمات کلیدی:
β, Titanium Yttrium Biomedical material Powder metallurgy Mechanical properties Acid