The influence of melt superheating treatment on the solidification characteristics and microstructure of Al–۲۰%Mg۲Si in-situ composite has been investigated. The results revealed that melt superheating temperature has a significant effect on solidification parameters and morphology of primary Mg۲Si particles. Solidification parameters acquired using cooling curve thermal analysis method, indicate that both nucleation temperature and nucleation undercooling of primary Mg۲Si particles increase by increasing melt superheating temperature, while recalescence undercooling decrease under the same condition. Also, based on the microstructural evaluations, melt superheating treatment can refine primary Mg۲Si particles and alter their morphology from dendritic shape to more spherical shape and the eutectic microstructure of a-Al + Mg۲Si becomes finer and the distance between eutectic layers becomes smaller.

Al–۲۰%Mg۲Si in-situ composite, melt superheating treatment, cooling curve thermal analysis, microstructure, solidification