N. Mohammed - Assistant professor, Thin Films Laboratory, College of Science, Mustansiriyah University, Baghdad, Iraq
H. f. Dagher

Thin films of meta-cinnabar mercuric sulfide (β-HgS) nanoparticles (NPs) was prepared by pulsed laser ablation (PLA) utilizing a pellet of cinnabar mercuric sulfide (α-HgS) was immersed in distilled water (DW). Q-switched Nd:YAG laser of ۱۰۶۴ nm wavelengths with repetition rate (۱hz) and fluency (۱.۵ J/cm۲) applied for ablation. Structural, morphological and particle sizes of the β-HgS NPs are invastigated by analyzing XRD, AFM, SEM and TEM measurements. Their crystal structure is transformed from hexagonal (wurtzite) of the α-HgS target material to cubic (zinc blende) β-HgS NPs. The optical properties of the β-HgS NPs are measured by UV–visible spectrophotometer. The direct band gap is calculated to be (۲.۴۵eV) of small particles (۴-۶.۲nm) moreover, the band gap value of smallest particles (۱-۴nm) is (۳.۴۷eV) according to the optical transmission spectra

Pulsed laser ablation, Nanocrystalline, Mercury sulfide, Cinnabar, Metacinnabar.