Production of Nano Leaded Brass Alloy by Oxide Materials
عنوان مقاله: Production of Nano Leaded Brass Alloy by Oxide Materials
شناسه ملی مقاله: ICNN02_491
منتشر شده در دومین کنگره بین المللی علوم و فناوری نانو در سال 1387
شناسه ملی مقاله: ICNN02_491
منتشر شده در دومین کنگره بین المللی علوم و فناوری نانو در سال 1387
مشخصات نویسندگان مقاله:
Iman Farahbakhsh - Islamic Azad University of Qouchan,Khorasan, Iran
S. Hadi Tabaian - Faculty of Metallurgy Engineering, Amirkabir University, Tehran
Jalil Vahdati Khaki - Department of Engineering, University Ferdowsi of Mashhad ,Mashhad
خلاصه مقاله:
Iman Farahbakhsh - Islamic Azad University of Qouchan,Khorasan, Iran
S. Hadi Tabaian - Faculty of Metallurgy Engineering, Amirkabir University, Tehran
Jalil Vahdati Khaki - Department of Engineering, University Ferdowsi of Mashhad ,Mashhad
In this study, formation of leaded brass by mechanochemical method is investigated using metal oxides and graphite as starting materials. Also, the effects of milling time and atmosphere on this process are evaluated. Alpha brass was produced when CuO, ZnO and PbO were milledunder argon atmosphere in the presence of graphite (as reducing agent). Concurrent reduction of zinc, copper and lead oxides took place in the argon atmosphere, whereas the reduction reactions did not proceed well in the closed chamber filled with air. These reactions were promoted by milling time up to 100 hours. The amount of reduction tends to decrease for longer times