Sogand Aghamohammadi - Department of Chemical Engineering, Faculty of Engineering, Azarbaijan Shahid Madani University, P.O.BOX ۵۳۷۵۱۷۱۳۷۹, Tabriz, Iran,
Mohsen Mohseni - Department of Chemical Engineering, Faculty of Engineering, Azarbaijan Shahid Madani University, P.O.BOX ۵۳۷۵۱۷۱۳۷۹, Tabriz, Iran,
Sajjad Abbasi - Department of Chemical Engineering, Faculty of Engineering, Azarbaijan Shahid Madani University, P.O.BOX ۵۳۷۵۱۷۱۳۷۹, Tabriz, Iran,
Sahar Rezaei - Department of Chemical Engineering, Faculty of Engineering, Azarbaijan Shahid Madani University, P.O.BOX ۵۳۷۵۱۷۱۳۷۹, Tabriz, Iran,
Alireza Hosseinzadeh - Department of Chemical Engineering, Faculty of Engineering, Azarbaijan Shahid Madani University, P.O.BOX ۵۳۷۵۱۷۱۳۷۹, Tabriz, Iran,
Yavuz Aydemir - Department of Chemical Engineering, Istanbul Technical University, Maslak ۳۴۴۶۹, Istanbul, Turkey

the high-temperature step required in the carbonization of organic precursors frequently impacts the distribution of the active phase, especially when high loadings are predicted. Metal-organic frameworks (MOFs) are a class of promising porous crystalline inorganic-organic hybrid materials that have appeared as one of the most rapidly developing fields in materials science and chemistry over the last two decades. MOFs have recently been presented as remarkable precursors in synthesizing amazingly distributed Co and Fe nanoparticles with fascinating performance in terms of activity, reactivity, and stability to solve the drawbacks of previous technologies. Because of its intriguing properties, nitrogen-rich ZIF-۶۷ is one of the most commonly used MOFs in this context. When pyrolyzed in an inert atmosphere, they produce carbon-encapsulated cobalt nanoparticles that inhibit the formation of larger agglomerates, favouring cobalt particle dispersion. Furthermore, when the pyrolysis conditions are optimized, the reducibility of cobalt nanoparticles can be increased even further. In the presented research, morphological characterization of plasma-assisted pyrolyzed ZIF-۶۷ will be taken in to account.

zeolite imidazole framework(ZIF-۶۷), Plasma, Morphology, carbonization