EFFECT OF FABRICATION PARAMETERS ON SYNTHESIS OF Ti۲AlC AND Ti۳AlC۲MAX PHASES BY MASHS
عنوان مقاله: EFFECT OF FABRICATION PARAMETERS ON SYNTHESIS OF Ti۲AlC AND Ti۳AlC۲MAX PHASES BY MASHS
شناسه ملی مقاله: JR_IJMSEI-11-4_007
منتشر شده در در سال 1393
شناسه ملی مقاله: JR_IJMSEI-11-4_007
منتشر شده در در سال 1393
مشخصات نویسندگان مقاله:
A. Sedghi - Materials Engineering Department, Imam Khomeini International University, Qazvin, Iran.
R. Vahed - Materials Engineering Department, Imam Khomeini International University, Qazvin, Iran.
خلاصه مقاله:
A. Sedghi - Materials Engineering Department, Imam Khomeini International University, Qazvin, Iran.
R. Vahed - Materials Engineering Department, Imam Khomeini International University, Qazvin, Iran.
Mechanically Activated Self-propagating High temperature Synthesis (MASHS) is the method which is used to promote self-propagating synthesis by increasing activity of reactants and increase the purity of products. In this study Ti ۲ AlC and Ti۳AlC۲ max phases were synthesized by using mechanically activated self-propagating high temperature synthesis (MASHS) and samples reactivity and phase structure of samples was studied. This process was performed by combination of short duration ball milling (MA) of reactants (Ti, Al and C as raw materials) and selfpropagating high temperature synthesis (SHS) by microwave or furnace. Mixtures of Ti/Al/C by mole ratio of ۲:۱:۱ and ۳:۱:۲ were milled for ۲h., then exothermic reaction was initiated in microwave or high temperature furnace and their reaction behavior and structure have been investigated by DTA and XRD. Results revealed that it’s possible to fabricate these materials by MASHS method but purity of them depends on type of reaction condition. DTA and XRD analyses proved that increasing of soaking time did not improve purity of compounds and some impurities such as TiC would be formed in non-optimized reaction routes.