E Enayati - Department of Chemistry, University of Islamic Azad
M Bagheri - Department of Physics, University of Kashan

The Bi۳+ and Mn۴+ cations were doped in Yttrium Iron Garnet (YIG) Y۳-xBixFe۵-xMnxO۱۲ (x=۰, ۰.۱, ۰.۲, ۰.۳, and ۰.۵) nanoparticles by a mechanochemical method. The experimental optimum time for ball milling was ۱۵ hours. To investigate the structure, size and shape of particles, the following techniques were used: X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results of the investigation of the crystal structure show that YIG nanoparticles with an average particle size of ۴۰ nm are formed in a single phase and with a cubic structure, and the best calcination temperature is about ۱۱۰۰°C for ۳ hours. This temperature is lower than the desired phase formation temperature in the conventional ceramic method. The maximum thermoluminescence response to the gamma rays of the ۶۰Co source was obtained in ۰.۳ mol% of the impurity. A computer program based on general-order kinetics was used to determine the number of peaks in the thermoluminescence radiation curve and the kinetic parameters related to each peak. Two overlapping peaks were observed at temperatures of ۳۹۸ and ۴۲۲ K in the thermoluminescence curve of this nanoparticle. The results show that this nanoparticle has suitable conditions for use in dosimetry

mechanochemi , TL, Kinetic parameters, Yttrium Iron Garnet, Dosimetry