The susceptibility to weld cracking of Ta-containing cast cobalt-based superalloy Mar-M302
Publish place: 1st International and 6th Joint Conference of Iranian Society of Metallurgical Engineers and the scientific community of Casting
Publish Year: 1391
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,497
This Paper With 13 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_037
تاریخ نمایه سازی: 8 بهمن 1391
Abstract:
The susceptibility to weld hot and cold cracking of Ta-containing cast cobalt based superalloy was studied. The microstructure of welded Mar-M302 cobalt based superalloy was investigated both autogenously and by usingfiller metal. Three different kinds of cracking were observed in the welded samples. It was found that; very hard and brittle eutectic has significant effects on base metal cracking during welding. The special type of microcracking observed in the eutectic, located in the heat affected zone(HAZ) of autogenous welds. Also the results revealed that when angular strains increased to the base metal elongation level, the cold macrocracks happened in filler metal welded samples in the opposite side of the weld line propagating along the eutectic areas. As a result the crack free repair welding procedure was achieved with controlling the metallurgical and mechanical parameters
Authors
M. Montazeri
Department of Materials Engineering, Tarbiat Modares University, P.O. Box ۱۴۱۱۵-۱۴۳, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :