Ti-Cr-N Coatings Deposited by Physical Vapor Deposition on AISI D۶ Tool Steels

Publish Year: 1391
نوع سند: مقاله ژورنالی
زبان: English
View: 55

This Paper With 7 Page And PDF Format Ready To Download

  • Certificate
  • من نویسنده این مقاله هستم

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این Paper:

شناسه ملی سند علمی:

JR_ISSIRAN-9-2_007

تاریخ نمایه سازی: 6 آبان 1402

Abstract:

In this study, physical vapor deposition (PVD) Ti-Cr-N coatings were deposited at two different temperatures ۱۰۰ and ۴۰۰ºC on hardened and tempered tool steel substrates. The influence of the applied deposition temperature on the physical and mechanical properties of coatings such as roughness, thickness, phase composition, hardness and Young’s modulus were evaluated. Phase compositions were studied by X-ray diffraction method. Mechanical properties were determined by Nano indentation. The results showed different behavior s in the mechanical properties by changing the deposition temperature. (Ti, Cr)N and TiN coatings consisted of only one solid solution cubic phase, while CrN coatings exhibited hexagonal Cr۲N and cubic CrN phases. Mechanical behavior of the (Ti, Cr)N coatings was related to the Ti content and their hardness reduced by decreasing the Ti content. (Ti, Cr)N coatings deposited at high temperature exhibited better mechanical properties compared to the coating deposited at low temperatures.

Authors

M. Akbarzadeh

Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran

A. Shafyei

Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran

H. Salimijazi

Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran

مراجع و منابع این Paper:

لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :
  • E.E. Vera, M. Vite, R. Lewis, E.A. Gallardo andJ.R. Laguna-Camacho: ...
  • P.H. Mayrhofer, C. Mitterer, L. Hultman and H ...
  • Clemens: Prog. Mater. Sci., ۵۱(۲۰۰۶), ۱۰۳۲ ...
  • Y.C. Chim, X.Z. Ding, X.T. Zeng and S. Zhang:Thin Solid ...
  • M.D. Drory and R.D. Evans: Surf. Coat ...
  • Technol., ۲۰۶(۲۰۱۱), ۱۹۸۳ ...
  • J.L. Mo and M.H. Zhu: Appl. Surf. Sci.,۲۵۵(۲۰۰۹), ۷۶۲۷ ...
  • S. Tan, X. Zhang, X. Wu, F. Fang and J. ...
  • A. Oztürk, K.V. Ezirmik, K. Kazmanlı, M ...
  • Ürgen, O.L. Eryılmaz and A. Erdemir: Tribol. Int.,۴۱(۲۰۰۸), ۴۹ ...
  • S.M. Aouadi, K.C. Wong, K.A.R. Mitchell, F ...
  • Namavar, E. Tobin, D.M. Mihut and S.L. Rohde:Appl. Surf. Sci., ...
  • L. Chen, S.Q. Wang, S.Z. Zhou, J. Li and Y.Z ...
  • Zhang: Int. J. Refract. Met. Hard. Mater., ۲۶(۲۰۰۸),[۱۰] M. Tamura ...
  • Technol., ۱۰۸–۱۰۹(۱۹۹۸), ۵۵۱ ...
  • S.Q. Wang, L. Chen, B. Yang, K.K. Chang, Y ...
  • Du, J. Li and T. Gang: Int. J. Refract. Met. ...
  • Mater., ۲۸(۲۰۱۰), ۵۹۳ ...
  • L. Chen, Y. Du, S.Q. Wang and J. Li: Int. ...
  • Refract. Met. Hard. Mater., ۲۵(۲۰۰۷), ۴۰۰ ...
  • K. Singh, P.K. Limaye, N.L. Soni, A.K. Grover,R.G. Agrawal and ...
  • Met. Hard. Mater., ۲۹(۲۰۱۱), ۲۶۸ ...
  • P. Wally, P. Ettmayer and W. Lengauer: J. AlloyCompd., ۲۲۸(۱۹۹۵), ...
  • J.G. Han, H.S. Myung, H.M: Lee and L.R ...
  • Shaginyan, Surf. Coat. Technol., ۱۷۴–۱۷۵(۲۰۰۳),[۱۷] P. Budzynski, J. Sielanko, Z. ...
  • Tarkowski, Vacuum, ۸۳(۲۰۰۹), ۱۸۶ ...
  • G. Ebersbach, D. Fabian, W. Wuttke and H.A ...
  • Jehn: Surf. Coat. Technol., ۵۹(۱۹۹۳), ۱۶۰ ...
  • R. Rother and H.A. Jehn: Surf. Coat. Technol.,۶۲(۱۹۹۳), ۶۳۵ ...
  • C.W. Teplin, M.F.A.M. van Hest, M. Dabney,C.L. Perkins, L.M. Gedvillas, ...
  • D.E. Wolfe, B.M. Gabriel and M.W. Reedy:Surf. Coat. Technol., ۲۰۵(۲۰۱۱), ...
  • X. Zeng, S. Zhang and J. Hsieh: Surf. Coat ...
  • Technol., ۱۰۲(۱۹۹۸), ۱۰۸ ...
  • G.A. Zhang, P.X. Yan, P. Wang, Y.M. Chen andJ.Y. Zhang: ...
  • B.D. Cullity and S.R. Stock: Elements of X-RayDiffraction, Prentice Hall, ...
  • W.C. Oliver and G.M: Pharr: Mater. Res.,۷(۱۹۹۲), ۱۵۶۴ ...
  • B. Warcholinski, A. Gilewicz, J. Ratajski, Z ...
  • Kuklinski and J. Rochowicz, Vacuum, ۲۳(۲۰۱۱),[۲۷] M. Ali, E. Hamzah, ...
  • K.H. Lee, C.H. Park, Y.S. Yoon and J.J. Lee:Thin Solid ...
  • V.M. Vishnyakov, V.I. Bachurin, K.F ...
  • Minnebaev, R. Valizadeh and D.G. Teer: Thin SolidFilms, ۴۹۷ (۲۰۰۶) ...
  • J. Vetter, H.J. Scholl and O. Knotek: Surf ...
  • Coat. Technol., ۷۴-۷۵(۱۹۹۵), ۲۸۶ ...
  • J.J. Nainaparampil, J.S. Zabinski and A ...
  • Korenyi-Both: Thin Solid Films, ۳۳۳(۱۹۹۸), ۸۸ ...
  • S.Y. Lee, G.S. Kim and J.H. Hahn: Surf. Coat ...
  • Technol., ۱۷۷–۱۷۸(۲۰۰۴), ۴۲۶ ...
  • Solid Films, ۳۳۲ (۱۹۹۸) ۲۴۰ ...
  • H. Hasegawa, A. Kimura and T. Suzuki: J. Vac ...
  • Sci. Technol. A, ۱۸(۲۰۰۰), ۱۰۳۸ ...
  • M. Ahlgren and H. Blomqvist: Surf. Coat ...
  • Technol., ۲۰۰(۲۰۰۵), ۱۵۷ ...
  • P.H. Mayrhofer, G. Tischler and C. Mitterer:Surf. Coat. Technol., ۱۴۲–۱۴۴(۲۰۰۱), ...
  • نمایش کامل مراجع